| Markenbezeichnung: | DLX |
| Modellnummer: | mit einer Breite von nicht mehr als 20 mm |
| MOQ: | 10 kg |
| Zahlungsbedingungen: | L/C, D/A, D/P, T/T, Western Union |
| Versorgungsfähigkeit: | 500 Tonnen pro Monat |
| Grade | Nickel (Ni)+ Cobalt (Co) | Copper (Cu) | Silicon (Si) | Manganese (Mn) | Carbon (C) | Magnesium (Mg) | Sulfur (S) | Phosphorus (P) | Iron (Fe) |
|---|---|---|---|---|---|---|---|---|---|
| N4/Ni201 | 99.9% | ≤0.015 | ≤0.03 | ≤0.002 | ≤0.01 | ≤0.01 | ≤0.001 | ≤0.001 | ≤0.04 |
| N6/Ni200 | 99.6% | 0.1 | 0.1 | 0.05 | 0.1 | 0.1 | 0.005 | 0.002 | 0.1 |
| Properties | N4/Ni201 | N6/Ni200 |
|---|---|---|
| Density | 8.9g/cm³ | 8.9g/cm³ |
| Melting Point | 1455°C | 1445-1470℃ |
| Coefficient of Thermal Expansion | 13.0µm/m*°C | 13.3×10⁻⁶/℃ |
| Thermal Conductivity | 10.1W/m*K | 90.7 W/m*K |
| Electrical Resistivity | 0.103×10⁻⁶Ω*/m (at 20℃) | |
| Electrical Conductivity | 14.6% IACS | |
| Tensile Strength | ≥450MPa | ≥450 MPa |
| Yield Strength | ≥200MPa | ≥150 MPa |
| Elongation at Break | ≥40% | ≥40% |
| Hardness | ≤150 |